Rapid isothermal processing of Si/sup +//P/sup +/ and Mg/sup +//P/sup +/ co-implantations into InP


Abstract:

The authors present the results of investigations on electrical properties of Si/sup +//P/sup +/ and Mg/sup +//P/sup +/ co-implanted InP wafers subjected to rapid isother...Show More

Abstract:

The authors present the results of investigations on electrical properties of Si/sup +//P/sup +/ and Mg/sup +//P/sup +/ co-implanted InP wafers subjected to rapid isothermal processing. It was found that a significant improvement of activation of Si and Mg in InP can be obtained by P/sup +/ co-implantations and rapid isothermal processing. The annealing cycle was at temperatures from 825 to 875 degrees C for 5 and 14 s. The maximum dopant activation and peak electron concentration for Si/sup +//P/sup +/ coimplants at doses of 1*10/sup 15//cm/sup 2/ were 70% and 5*10/sup 19/ cm/sup 3/. A high hole concentration of 1.1*10/sup 19//cm/sup 3/ was obtained by Mg/sup +//P/sup +/ coimplantations.<>
Published in: IEEE Transactions on Electron Devices ( Volume: 39, Issue: 1, January 1992)
Page(s): 209 - 211
Date of Publication: 06 August 2002

ISSN Information:

References is not available for this document.

Select All
1.
M. V. Rao and M. P. Keating, "Si- and Be-implantations in InP:Fe activated by halogen lamp rapid thermal annealing", J. Electron. Mat., vol. 17, pp. 315, July 1988.
2.
R. Heckingbottom and T. Ambridge, "Ion implantation in compound semiconductors—an approach based on solid state theory", Rad. Effects, vol. 17, pp. 31, Jan. 1973.
3.
A. Dodabalapur and B. G. Slreetinan, "Rapid thermal annealing of dual Si and P implants in TnP", J. Electron. Mat., vol. 18, pp. 65, Jan. 1989.
4.
K. Wang, "Formation of a shallow p+ layer on InP using a P/Be coimplant", Appl. Phys. Lett., vol. 51, pp. 2127, Dec. 1987.
5.
H. Shen, G. Yang, Z. Zhou and S. Zou, "Improved activation in Si+ and P+ dually implanted InP", Semicond. Sci. Technol., vol. 4, pp. 951, Nov. 1989.
6.
J. P. Donnelly and C. E. Hurwitz, "The electrical characteristics of InP implanted with the column IV elements", Solid State Electron, vol. 23, pp. 1151, Nov. 1980.
7.
D. E. Davies, "Implantation in InP", J. Crystal Growth, vol. 54, pp. 150, July 1981.
8.
M. V. Rao and R. K. Nadella, "Be+ /P+ Be+/Ar+ and Be+/N+ coimplantations into InP: Fe", J. Appl. Phys., vol. 67, pp. 1761, Feb. 1990.

References

References is not available for this document.