Rapid isothermal processing of Si/sup +//P/sup +/ and Mg/sup +//P/sup +/ co-implantations into InP


Abstract:

The authors present the results of investigations on electrical properties of Si/sup +//P/sup +/ and Mg/sup +//P/sup +/ co-implanted InP wafers subjected to rapid isother...Show More

Abstract:

The authors present the results of investigations on electrical properties of Si/sup +//P/sup +/ and Mg/sup +//P/sup +/ co-implanted InP wafers subjected to rapid isothermal processing. It was found that a significant improvement of activation of Si and Mg in InP can be obtained by P/sup +/ co-implantations and rapid isothermal processing. The annealing cycle was at temperatures from 825 to 875 degrees C for 5 and 14 s. The maximum dopant activation and peak electron concentration for Si/sup +//P/sup +/ coimplants at doses of 1*10/sup 15//cm/sup 2/ were 70% and 5*10/sup 19/ cm/sup 3/. A high hole concentration of 1.1*10/sup 19//cm/sup 3/ was obtained by Mg/sup +//P/sup +/ coimplantations.<>
Published in: IEEE Transactions on Electron Devices ( Volume: 39, Issue: 1, January 1992)
Page(s): 209 - 211
Date of Publication: 06 August 2002

ISSN Information:

No metrics found for this document.

Usage
Select a Year
2025

View as

Total usage sinceJan 2011:24
00.20.40.60.811.2JanFebMarAprMayJunJulAugSepOctNovDec100000000000
Year Total:1
Data is updated monthly. Usage includes PDF downloads and HTML views.

References

References is not available for this document.