Field emission characterization of in-situ deposited metallic nanocones

An in-situ fabrication technique based on ion track etched template electrodeposition of metallic nanocones was used for the production of field emitter cathodes. Gold nanocones with a height of 24 microns, a base diameter between 3 to 4 microns and a tip diameter below 300 nanometers were deposited on a circular electrode with a diameter of 2.5 mm. The integral field emission (FE) measurements of samples with cone densities of 6 · 10
⁴
cones/cm
²
(sample A) and 1 · 10
⁶
cones/cm
²
(sample B) yielded in a maximum current of 37.5 μA at an applied field of 12.5 V/μm for sample A and 29.1 μA at 9.4 V/μm for sample B. The stability of emission current was investigated for over 48 hours and no degradation was observed.