Study of intermetallic compounds isostructural to MgB/sub 2/

The small intergrain effect of MgB/sub 2/ on supercurrent makes it one of the most promising candidates for superconducting conductors due to its easier processing and the associated lower manufacturing cost. Unfortunately, the superconducting transition temperature T/sub c/ is only 40 K. However, band-structure calculations predict that a higher T/sub c/ than that of MgB/sub 2/ is possible for isostructural and isovalent intermetallic compounds with greater lattice parameters or greater unit cell volumes. The prediction appears to be consistent with the negative pressure effect on T/sub c/ observed. The substitution of the larger Ca-ions for the smaller Mg-ions has thus been suggested to raise T/sub c/, but not yet realized. Alternatively, we have synthesized and studied a series of binary and pseudobinary intermetallic compounds, AGa/sub 2/, AGa/sub 2-x/Si/sub x/, and AAl/sub 2-x/Si/sub x/, where A=Ca, Sr, or Ba, which are isostructural to MgB/sub 2/ and have greater lattice parameters than MgB/sub 2/. In spite of the greater lattice parameters, AGa/sub 2/ are not superconducting. However, all pseudobinary compounds AGa/sub 2-x/Si/sub x/ and AAl/sub 2-x/Si/sub x/ for 0.6