GeSn p-FinFETs with Sub-10 nm Fin Width Realized on a 200 mm GeSnOI Substrate: Lowest SS of 63 mV/decade, Highest Gm,int of 900 µS/µm, and High-Field µeff of 275 cm2/V•s

We report the first GeSn p-FinFETs with sub-10 nm fin width (W
_Fin
) enabled by the formation of the first 200 mm GeSn-on-insulator (GeSnOI) substrate and a self-limiting digital etch for accurate control of the fin dimension, achieving a fin with a top width of 5 nm. Owing to the excellent gate control using extremely scaled GeSn fin and the good GeSn fin quality maintained using a device fabrication process with low thermal budget, an SS of 63 mV/decade was achieved at channel length (L
_CH
) of 50 nm, which is a record low for Ge-based p-FETs. Furthermore, record high G
_m,int
of 900 μS/μm (V
_DS
of -0.5 V) and G
_m,int
/S
_sat
of 10.5 for GeSn p-FETs were achieved. A high high-field hole mobility μ
_eff
of 275 cm
²
/V·s (at inversion carrier density N
_inv
of 8×10
¹²
cm
^-2
) was also obtained.