Inverted Type-I CdS/CdSe Core/Crown colloidal quantum ring

Inverted Type-I quantum rings (QRs) are a recently developed class of nanostructure in which a lower bandgap material is laterally grown as a crown of same thickness around a higher bandgap nanoplatelet (NPL) core [l·2]· e.g. core/crown CdS/CdSe as shown in Fig. 1(a). For this work, we have colloidally synthesized 3 monolayer (ML) thick CdS/CdSe QR samples using seed-mediated method, by using 3ML CdS NPLs as the core seed [3]. Subsequently, continuous injection of Se precursor, elemental Se dissolved in octadecene (ODE), Cd precursor and Cd(CH3CO2)2 led to the growth of CdSe crown. The ring width was controlled by tuning the injection amount to regulate the extent of the lateral size of the crown coating. A TEM image of the 3ML CdS/CdSe QRs is shown in Fig. 1(b)· which suggests atomically flat lateral growth of CdSe on CdS NPLs, as it has larger average lateral size (30±10 nm) compared to the CdS core only NPLs. We have measured the photoluminescence (PL) and absorption spectra of CdS/CdSe QRs at different phases of crown growth. Fig. 1(c) shows the PL and absorption spectra for two contrasting cases having a (i) thin, and a (ii) thick CdSe crown. As the crown thickness increases, there is lesser extent of lateral confinement, and thus a red-shift in the PL peak position. Also the linewidth of the emission spectra narrows down as more CdSe is deposited in the crown. This is owing to the randomly dispersed CdSe islands of varying sizes formed around the CdS NPLs at the initial phase of the CdSe crown growth resulting in a normal distribution of energy levels. For a sufficiently thick CdSe crown, the electronic structure and optical properties of CdS/CdSe QR is identical to CdSe NPLs alone, characterized by narrower linewidths. Moreover, we have verified that the emission peak of the 3ML CdS/CdSe QRs is spectrally tunable between the peak emissions of 3ML CdS NPL core only (382 nm) and 3 ML CdSe NPL core only (462 nm). In terms of the absorption spectra, as we begin to grow the CdSe crown, there is a gradual emergence of the primary and secondary CdSe absorption peaks at 460 nm (electron-heavy hole) and 431 nm (electron-light hole) respectively, as can be seen in Fig. 1(c-ii). On the other hand, for thin CdSe crowns, these peaks are undeterminable, while the overlapping primary and secondary absorption peaks of CdS at 382 nm (electron-heavy hole) and 373 nm (electron-light hole) are more prominent, as can be seen in Fig. 1(c-i).