Annealing Effect of FeSe Superconducting Polycrystalline Bulks in Low Oxygen Atmosphere

FeSe superconducting bulks with different Fe contents were prepared by high energy ball milling aided sintering process followed by a post annealing process in low oxygen atmosphere. The influences of Fe content, annealing temperature and oxygen partial pressure have been systematically studied. It was found that both the critical temperature and superconducting phase volume ratio have been obviously improved with annealing. However, the effect of oxygen annealing process on FeSe polycrystalline bulks was different with that on FeSe single crystals. In polycrystalline bulks, the annealing process could further promote the phase transition from nonsuperconducting hexagonal δ-FeSe phase to superconducting tetragonal β-FeSe phase. Meanwhile, the chemical composition uniformity has also been enhanced with no obvious FeO
_δ
phase detected by X-Ray Diffraction. With optimized annealing process under the oxygen partial pressure of 5% at 400 °C for 10 h, FeSe superconducting bulks have reached the critical temperature of 9.1 K.