Thickness variation of breakdown field strength in plasma oxidized aluminum films

The breakdown field strength in plasma oxidized Al
2
O
3
films ranging in thickness from 15 to 600 Å, was observed to exhibit a dependence proportional to s
^-1/4
, where s is oxide thickness. This variation was found to be temperature independent.